recommended you read replica watches. Online Store fake rolex watches. navigate to this web-site www.heroreplica.com. check here https://www.glowreplica.com/. important site replicas de relogios. look at here https://www.rolexreplikizegarkow.pl/. check out this site fake-richardmille. see here now https://richardmillecheap.com/. look at this website https://www.watchesjob.com/. more noob replica watches for sale. check my source homeswatches.com. offer watch replicas USA. read this noob replica watches. blog link replica patek philip. this link bell and ross replica. sites richard mille replica ebay. look at more info richardmillecarbon.com. basics https://www.pussywatches.com/. Top brand replica bell and ross.

IHOA Chemical FOAM | EVA | AT | PU | PE
(KR) 070-4076-0053 / (VN) 0274-371-2765

P.U SPONGE SPEC

Polyurethane formulations cover an extremely wide range of stiffness, hardness, and densities. Polyurethane products have many uses. Over three quarters of the global consumption of polyurethane products is in the form of foams, with flexible and rigid types being roughly equal in market size. In both cases, the foam is usually behind other materials: flexible foams are behind upholstery fabrics in commercial and domestic furniture; rigid foams are inside the metal and plastic walls of most refrigerators and freezers, or behind paper, metals and other surface materials in the case of thermal insulation panels in the construction sector. Its use in garments is growing : for example, in lining the cups of brassieres. Polyurethane is also used for moldings which include door frames, columns, balusters, window headers, pediments, medallions and rosettes.

[P.U. Foam Spec.]

14kg

22kg

26kg

30kg

50kg

Filter

MEMORY

Apparent Density

kg/m3

14

22

25.8

30

50

30.35

73.92

25% ILD

kg/314m3

6

25

27

30

42

13.78

30

Ball Rebound

%

35

35

31

28

35

 

11

Tensile Strength

kg/cm2

0.8

1

1.6

2.2

3

1.3

2.5

Elongation

%

120

90

83

80

85

160.73

140

Tear Strength

kg/cm

0.35

0.5

0.7

0.8

0.9

0.74

1.5